Aluminium alloys have the possibility to be infinitely recycled. By only generating 5% of the emissions compared to primary aluminium, great CO2 savings can be made. One of the issues in manufacturing components entirely from post-consumer scrap is the presence of trace elements and impurities. Such elements can be Fe, Cu, Cr, P and Pb. In sheet metal manufacturing, these elements can also react with process agents such as Ti, B, Na and Sr and affect the recrystallization behavior and in turn mechanical properties.In this work, a derivative of the 3003 alloy made entirely from post-consumer scrap has been analysed. The alloy achieved insufficient formability due to lack of recrystallization and grain growth. With the use of scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS) and electron backscatter diffraction (EBSD) together with focused ion beam (FIB) lamella preparation, the microstructure was characterized.The characterization shows both larger particles of α-Al15Si2M4 (M=Mn,Fe,Cr) from solidification and dispersoids from heat treatment, pinning the grain boundary movement together with Q-AlCuMgSi. With the use of high throughput computational thermodynamics, Thermo-Calc was used to effectively screen compositions lowering the amount of α-Al15Si2M4 and removing the Q-AlCuMgSi phase. The new alloy was cast using directional solidification at different cooling rates to study the particle morphology, which in turn plays a role in the particle break up and distribution during cold working as the interparticle spacing affects the grain growth.Varying cooling rates was seen to affect morphology and distribution. Hot compression was utilized to examine the particle redistribution before cold work. It was however shown that hot compression was not sufficient in redistributing the particles as would be the case in rolling.